    "condition": 0,
    "source_row": 3,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 203.99885,
    "strain_percent": 41.56149
  },
  {
    "condition": 0,
    "source_row": 4,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 123.97847,
    "strain_percent": 15.2662
  },
  {
    "condition": 0,
    "source_row": 5,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 152.72564,
    "strain_percent": 39.09498
  },
  {
    "condition": 0,
    "source_row": 6,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 144.06444,
    "strain_percent": 18.74054
  },
  {
    "condition": 0,
    "source_row": 7,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 170.68839,
    "strain_percent": 54.02385
  },
  {
    "condition": 0,
    "source_row": 8,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 146.96012,
    "strain_percent": 36.16747
  },
  {
    "condition": 0,
    "source_row": 9,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 172.88668,
    "strain_percent": 45.31129
  },
  {
    "condition": 0,
    "source_row": 10,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 236.13014,
    "strain_percent": 61.16285
  },
  {
    "condition": 0,
    "source_row": 11,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 206.39885,
    "strain_percent": 44.16849
  },
  {
    "condition": 0,
    "source_row": 12,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 220.59483,
    "strain_percent": 53.2193
  },
  {
    "condition": 0,
    "source_row": 13,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 243.07791,
    "strain_percent": 57.25463
  },
  {
    "condition": 0,
    "source_row": 14,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 216.04034,
    "strain_percent": 34.96908
  },
  {
    "condition": 0,
    "source_row": 15,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 181.70181,
    "strain_percent": 47.63064
  },
  {
    "condition": 0,
    "source_row": 16,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 236.2316,
    "strain_percent": 67.70337
  },
  {
    "condition": 0,
    "source_row": 17,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 272.65553,
    "strain_percent": 59.53672
  },
  {
    "condition": 0,
    "source_row": 18,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 179.23486,
    "strain_percent": 55.34711
  },
  {
    "condition": 0,
    "source_row": 19,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 216.2956,
    "strain_percent": 49.55772
  },
  {
    "condition": 0,
    "source_row": 20,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 197.27648,
    "strain_percent": 48.24344
  },
  {
    "condition": 0,
    "source_row": 21,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 260.95245,
    "strain_percent": 59.09566
  },
  {
    "condition": 0,
    "source_row": 22,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 225.36872,
    "strain_percent": 42.11741
  },
  {
    "condition": 0,
    "source_row": 23,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 280.03361,
    "strain_percent": 56.43091
  },
  {
    "condition": 0,
    "source_row": 24,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 245.96369,
    "strain_percent": 62.46891
  },
  {
    "condition": 0,
    "source_row": 25,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 155.91501,
    "strain_percent": 33.3285
  },
  {
    "condition": 0,
    "source_row": 26,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 175.02707,
    "strain_percent": 42.77975
  },
  {
    "condition": 0,
    "source_row": 27,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 180.7668,
    "strain_percent": 39.31735
  },
  {
    "condition": 0,
    "source_row": 28,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 206.58419,
    "strain_percent": 35.69423
  },
  {
    "condition": 0,
    "source_row": 29,
    "source_columns": [
      3,
      4
    ],
    "draw_ratio": 7.5,
    "fracture_stress_MPa": 240.56681,
    "strain_percent": 55.75916
  },
  {
    "condition": 1,
    "source_row": 3,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 254.46398,
    "strain_percent": 40.82218
  },
  {
    "condition": 1,
    "source_row": 4,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 189.46967,
    "strain_percent": 18.61916
  },
  {
    "condition": 1,
    "source_row": 5,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 284.1154,
    "strain_percent": 31.85626
  },
  {
    "condition": 1,
    "source_row": 6,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 201.44991,
    "strain_percent": 24.58224
  },
  {
    "condition": 1,
    "source_row": 7,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 235.30115,
    "strain_percent": 47.05842
  },
  {
    "condition": 1,
    "source_row": 8,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 313.36072,
    "strain_percent": 65.12308
  },
  {
    "condition": 1,
    "source_row": 9,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 461.37508,
    "strain_percent": 43.39743
  },
  {
    "condition": 1,
    "source_row": 10,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 185.15576,
    "strain_percent": 20.8442
  },
  {
    "condition": 1,
    "source_row": 11,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 279.5819,
    "strain_percent": 41.29889
  },
  {
    "condition": 1,
    "source_row": 12,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 193.82714,
    "strain_percent": 32.6616
  },
  {
    "condition": 1,
    "source_row": 13,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 181.30075,
    "strain_percent": 31.44723
  },
  {
    "condition": 1,
    "source_row": 14,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 206.40796,
    "strain_percent": 35.71153
  },
  {
    "condition": 1,
    "source_row": 15,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 273.31176,
    "strain_percent": 49.33065
  },
  {
    "condition": 1,
    "source_row": 16,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 242.89496,
    "strain_percent": 36.84459
  },
  {
    "condition": 1,
    "source_row": 17,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 318.92956,
    "strain_percent": 39.72119
  },
  {
    "condition": 1,
    "source_row": 18,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 306.05771,
    "strain_percent": 48.04885
  },
  {
    "condition": 1,
    "source_row": 19,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 251.41487,
    "strain_percent": 35.66749
  },
  {
    "condition": 1,
    "source_row": 20,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 287.28666,
    "strain_percent": 39.12668
  },
  {
    "condition": 1,
    "source_row": 21,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 327.50824,
    "strain_percent": 48.35038
  },
  {
    "condition": 1,
    "source_row": 22,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 263.11469,
    "strain_percent": 38.48385
  },
  {
    "condition": 1,
    "source_row": 23,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 241.91569,
    "strain_percent": 31.16029
  },
  {
    "condition": 1,
    "source_row": 24,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 217.4162,
    "strain_percent": 28.85266
  },
  {
    "condition": 1,
    "source_row": 25,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 302.09327,
    "strain_percent": 36.40361
  },
  {
    "condition": 1,
    "source_row": 26,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 297.0393,
    "strain_percent": 35.47383
  },
  {
    "condition": 1,
    "source_row": 27,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 299.67465,
    "strain_percent": 37.27442
  },
  {
    "condition": 1,
    "source_row": 28,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 312.5143,
    "strain_percent": 45.68872
  },
  {
    "condition": 1,
    "source_row": 29,
    "source_columns": [
      7,
      8
    ],
    "draw_ratio": 10.0,
    "fracture_stress_MPa": 252.98054,
    "strain_percent": 43.07028
  },
  {
    "condition": 2,
    "source_row": 3,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 326.30835,
    "strain_percent": 31.60254
  },
  {
    "condition": 2,
    "source_row": 4,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 315.50383,
    "strain_percent": 24.71763
  },
  {
    "condition": 2,
    "source_row": 5,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 311.51255,
    "strain_percent": 24.72815
  },
  {
    "condition": 2,
    "source_row": 6,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 277.61373,
    "strain_percent": 23.56082
  },
  {
    "condition": 2,
    "source_row": 7,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 308.06825,
    "strain_percent": 29.45634
  },
  {
    "condition": 2,
    "source_row": 8,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 303.19326,
    "strain_percent": 35.89898
  },
  {
    "condition": 2,
    "source_row": 9,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 307.1137,
    "strain_percent": 32.23196
  },
  {
    "condition": 2,
    "source_row": 10,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 286.62211,
    "strain_percent": 26.7444
  },
  {
    "condition": 2,
    "source_row": 11,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 343.9795,
    "strain_percent": 32.06454
  },
  {
    "condition": 2,
    "source_row": 12,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 318.49281,
    "strain_percent": 29.96573
  },
  {
    "condition": 2,
    "source_row": 13,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 329.55614,
    "strain_percent": 31.5183
  },
  {
    "condition": 2,
    "source_row": 14,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 326.49159,
    "strain_percent": 33.02885
  },
  {
    "condition": 2,
    "source_row": 15,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 320.52313,
    "strain_percent": 27.8056
  },
  {
    "condition": 2,
    "source_row": 16,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 258.01109,
    "strain_percent": 6.198
  },
  {
    "condition": 2,
    "source_row": 17,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 343.72297,
    "strain_percent": 16.39948
  },
  {
    "condition": 2,
    "source_row": 18,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 317.34608,
    "strain_percent": 27.9549
  },
  {
    "condition": 2,
    "source_row": 19,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 351.76107,
    "strain_percent": 37.70186
  },
  {
    "condition": 2,
    "source_row": 20,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 322.00578,
    "strain_percent": 35.02643
  },
  {
    "condition": 2,
    "source_row": 21,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 273.66765,
    "strain_percent": 8.04686
  },
  {
    "condition": 2,
    "source_row": 22,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 334.20654,
    "strain_percent": 28.00735
  },
  {
    "condition": 2,
    "source_row": 23,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 254.44247,
    "strain_percent": 23.662
  },
  {
    "condition": 2,
    "source_row": 24,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 309.85722,
    "strain_percent": 32.21534
  },
  {
    "condition": 2,
    "source_row": 25,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 284.03706,
    "strain_percent": 32.04801
  },
  {
    "condition": 2,
    "source_row": 26,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 286.11642,
    "strain_percent": 27.49051
  },
  {
    "condition": 2,
    "source_row": 27,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 282.40992,
    "strain_percent": 30.55573
  },
  {
    "condition": 2,
    "source_row": 28,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 318.46925,
    "strain_percent": 27.80665
  },
  {
    "condition": 2,
    "source_row": 29,
    "source_columns": [
      11,
      12
    ],
    "draw_ratio": 12.5,
    "fracture_stress_MPa": 273.67226,
    "strain_percent": 12.06497
  },
  {
    "condition": 3,
    "source_row": 3,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 369.41366,
    "strain_percent": 17.17008
  },
  {
    "condition": 3,
    "source_row": 4,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 447.4434,
    "strain_percent": 21.81205
  },
  {
    "condition": 3,
    "source_row": 5,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 435.1532,
    "strain_percent": 22.30682
  },
  {
    "condition": 3,
    "source_row": 6,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 371.36164,
    "strain_percent": 19.66508
  },
  {
    "condition": 3,
    "source_row": 7,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 393.9396,
    "strain_percent": 24.14095
  },
  {
    "condition": 3,
    "source_row": 8,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 302.36303,
    "strain_percent": 15.90611
  },
  {
    "condition": 3,
    "source_row": 9,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 368.74135,
    "strain_percent": 23.60692
  },
  {
    "condition": 3,
    "source_row": 10,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 283.03101,
    "strain_percent": 13.21775
  },
  {
    "condition": 3,
    "source_row": 11,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 387.00773,
    "strain_percent": 17.33469
  },
  {
    "condition": 3,
    "source_row": 12,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 345.86296,
    "strain_percent": 17.41536
  },
  {
    "condition": 3,
    "source_row": 13,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 350.72158,
    "strain_percent": 18.88452
  },
  {
    "condition": 3,
    "source_row": 14,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 394.59595,
    "strain_percent": 21.31819
  },
  {
    "condition": 3,
    "source_row": 15,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 405.13367,
    "strain_percent": 20.63387
  },
  {
    "condition": 3,
    "source_row": 16,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 376.98657,
    "strain_percent": 22.75903
  },
  {
    "condition": 3,
    "source_row": 17,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 315.04034,
    "strain_percent": 18.20094
  },
  {
    "condition": 3,
    "source_row": 18,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 303.84108,
    "strain_percent": 15.7152
  },
  {
    "condition": 3,
    "source_row": 19,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 309.20349,
    "strain_percent": 14.12028
  },
  {
    "condition": 3,
    "source_row": 20,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 308.52644,
    "strain_percent": 10.0938
  },
  {
    "condition": 3,
    "source_row": 21,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 300.96992,
    "strain_percent": 5.69867
  },
  {
    "condition": 3,
    "source_row": 22,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 327.7943,
    "strain_percent": 14.04874
  },
  {
    "condition": 3,
    "source_row": 23,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 345.65845,
    "strain_percent": 14.98753
  },
  {
    "condition": 3,
    "source_row": 24,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 316.18263,
    "strain_percent": 15.10724
  },
  {
    "condition": 3,
    "source_row": 25,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 336.21072,
    "strain_percent": 17.55651
  },
  {
    "condition": 3,
    "source_row": 26,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 346.91542,
    "strain_percent": 14.6258
  },
  {
    "condition": 3,
    "source_row": 27,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 323.87926,
    "strain_percent": 17.93414
  },
  {
    "condition": 3,
    "source_row": 28,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 367.64776,
    "strain_percent": 21.79574
  },
  {
    "condition": 3,
    "source_row": 29,
    "source_columns": [
      15,
      16
    ],
    "draw_ratio": 15.0,
    "fracture_stress_MPa": 330.76466,
    "strain_percent": 18.25046
  }
]